Low Carbon (LC) Steel Shot has proven to have been a cost-effective choice for end users. The bainitic - martensite microstructure is achieved by meticulous raw material selection, constant monitoring of metallurgical chemistry and a controlled atomization process. Abrasive durability has been reported up to 20% higher than standard high carbon shot with no loss of cleaning efficiency.
Longer Life with Excellent Performance:
LC Steel Shot does not have inner crack. Thus, its life span is much longer than High Carbon Steel Shot
Cost Saving: Customer can save maintenance cost of machine and blade as it does not break into pieces throughout the most of blasting process. Saving comprehensive usage cost by 30-70%. Cleaning effeciency improves by 35%. The coating adhesion reaches 20MPa
Low Carbon Emission: It is environment-friendly due to low carbon content. 90% recyclable and 70% less dust emmision.
Higher strength, high tenacity and longer service life. Higher resistance to shattering on impact.
Higher corrosion resistance: No slag filled surface cracks.
Lower wear on machine parts and longer life of accessories.
Durability up to 30% higher than high carbon shot.
Technical specifications:
| Carbon | 0.05 to 0.20 % |
| Silicon | 0.10 to 0.30 % |
| Manganese | 0.35 to 1.50 % |
| Phosphorous | 0.03 % maximum |
| Sulphur | 0.03 % maximum |
| Hardness | 40 – 52 HRC in working condition |
| Microstructure | Duplex structure of Bainite & Martensite |
| Density | ≤ 7.50 g/cc |
For further information, you can contact our Sales Engineer, or you can contact us directly or here.