Steel Fibre dalam berbagai bentuk antara lain
Material ME Fibre, Cold Drawn Fibre dan Stainless Steel Wool bisa dibuat dengan menggunakan material SUS 430, SUS 446, SUS 304, SUS 310, SUS 316 maupun SUS 330.
Specifications:
| Grades | 330 | 310 | 304 | 446 | 430 | 430A* | |
|---|---|---|---|---|---|---|---|
| Chemical Composition | C | 0.5 | 0.50 | 0.50 | 0.40 | 0.40 | 0.40 |
| P | 0.05 | 0.05 | 0.05 | 0.05 | 0.05 | 0.05 | |
| Mn | 2.0 | 2.0 | 2.0 | 2.0 | 2.0 | 2.0 | |
| Si | 3.5 | 3.5 | 3.5 | 3.5 | 3.5 | 3.5 | |
| Cr | 17.0 - 20.0 | 24.0 - 26.0 | 18.0 - 20.0 | 23.0 - 27.0 | 14.0 - 18.0 | 14.0 - 18.0 | |
| Ni | 34.0 - 37.0 | 19.0 - 22.0 | 8.0 - 10.5 | 0.5 | 0.5 | 0.5 | |
| Al | - | - | - | - | - | 2-4 | |
| Melt temperature °C | 1343 - 1425 | 1400 - 1455 | 1400 - 1455 | 1425 - 1510 | 1480 - 1530 | 1520 - 1560 | |
| Thermal conductivity (540°C) W/m2K | 28.50 | 20.1 | 21.5 | 24.8 | 26.5 | ||
| Coefficient of thermal expansion (870°C) @10-6/°C | 17.6 | 18.50 | 20.2 | 13.1 | 13.7 | ||
| Critical Oxidation Temperature | Cyclic heating | 1050°C | 1040°C | 870°C | 1100°C | 850°C | |
| Continuous Service | 1165°C | 1200°C | 1100°C | 1200°C | 1000°C | ||
| Tensile Strength | 20°C | 480 MPa | 540 MPa | 515 MPa | 900 Mpa | 850 Mpa | |
| 870°C | 31 Mpa | 152 MPa | 124 Mpa | 53 Mpa | 47 Mpa | ||
| Modulus of Elasticity (24°C) | 196 Gpa | 125 GPa | 124 GPa | 97 Gpa | 83 Gpa | ||
Grade 430A merupakan jenis ME Stainless Steel Fibres yang banyak digunakan di Jepang. Mengandung alumunium dan mempunyai melting point yang lebih tinggi dari yang lainnya.
Keuntungan grade 430 A adalah mempunyai tingkat kondensasi yang lebih rendah, kekerasan yang lebih tinggi, kemampuan gesek yang lebih tinggi dan mempunyai kemampuan tahan terhadap oksidasi dari grade lainnya (sekitar 3-6 kali).
Untuk informasi lebih lanjut bisa menghubungi Sales Engineer kami, atau bisa menghubungi kami secara langsung atau di sini.